Wide spectrum - High light intensity - Focused light
2 modes :
- High Mode : 2300-2500 mw/cm² - curing 2mm resin in 1s
- Standard Mode : 1000-1200 mw/cm²
- 360° curing : reach every angle
- Wave band 385 - 515 nm (blue light) : better curing of the resin materials containing photoinitiators such as TPO.
- Metal head : anti-shock, never cracks
- Ultra light : 259g only
Overheat protection: after 400 seconds of continuous use, the unit automatically pauses fo 60 seconds, ensuring safe operation
Specifications :
Light intensity : 1.000 – 1.200 mW/cm² and 2.300 – 2.500 mW/cm²
Wave band : 385 - 515 nm
Lens diameter : 10mm
Weight : 259 gr
Dimensions : 268.8mm x 26.1mm x 31.8mm
ESCOM 250 is a light-curing hybrid composite designed for anterior and posterior restorations. It combines excellent mechanical strength with natural aesthetics.
Ideal for Class I to V restorations, it allows easy sculpting and optimal polishing. Available in a 4 g syringe, it ensures precise application thanks to its ergonomic tip.
Featuring excellent sculptability, ESCOM 250 remains fully workable under ambient light for up to 90 seconds before polymerization, allowing comfortable and controlled handling.
Clinical Advantages
Versatility
ESCOM 250 can be used in a wide range of direct and indirect restorative procedures:
- Anterior and posterior restorations
- Class I to V restorations
- Indirect restorations (veneers)
- Undercut elimination
- Repair of ceramic and composite veneers
- Core build-ups
- Splinting
Aesthetics
ESCOM 250 provides an excellent mimetic effect thanks to its shade range and minimal color change before and after light curing, ensuring a natural and stable result.
Reliability
ESCOM 250 features outstanding physical properties:
- Fracture strength: 350 MPa
- Compressive strength: 328 MPa
- Flexural strength: 135 MPa
- Polymerization shrinkage: 1.09%
- Low material shrinkage
- Bisphenol-free
- Light-cure for 10seconds (LED 1200mW /cm²)
Composition:
- Monomers: Bis-GMA, UDMA, TEGDMA
- Inorganic fillers: Zirconia particles (16 nm to ~1.2 µm), barium glass, fumed silica
- Filler content: 60% by volume
- Additives: Initiators, catalysts, stabilizers, and other agents